About 316 stainless steel elbow knowledge

　　The maximum carbon content of 316 stainless steel elbow is 0.03, which can be used for annealing after annealing and for maximum corrosion resistance. 316 and 317 stainless steel (317 stainless steel after performance) is molybdenum containing Stainless Steel Elbows. The total performance of the steel is better than that of 310 and 304 stainless steel. When the concentration of sulfuric acid is lower than 15% and higher than 85% at high temperature, 316 stainless steel has wide application. 316 stainless steel also has good chloride corrosion properties, so it is usually used in marine environment. Stainless Steel Seamless 180 degree Pipe Fitting Butt Weld Elbow is also named 00Cr17Ni14Mo2 corrosion resistance: corrosion resistance is better than 304 stainless steel, and it has good corrosion resistance in the process of pulp and paper production.

　　Moreover, 316 stainless steel is also resistant to erosion of the marine and corrosive industrial atmosphere. Stainless Steel Elbows has good oxidation resistance when it is used intermittently below 1600 degrees of heat and under 1700 degrees of continuous use. In the range of 800-1575 degrees, it is best not to continue to act on 316 stainless steel continuously, but the stainless steel has good heat resistance when 316 stainless steel is used continuously outside the range of temperature. The resistance of 316 stainless steel to carbide precipitation is better than that of 316 stainless steel, which can be used in the above temperature range.